With two-part HS clear coats and two-part HS top coat, the
Matting Component - LVM 769 810 A2- creates a matted top coat
coating for metal and plastic finishes. |
Areas of application include large surfaces/complete
painting as well as small- and attachment parts. |
Hardened, well-preserved and sanded old paint or factory
paints |
Primed and filled metal- and plastic parts |
Note
For information about plastic parts, refer to "The VW/Audi
Coating System for Plastic Parts" (Data Sheet 5.74). |
Two-Part HS Clear Coat -L2K 769 500 A5- |
Two-Part HS Vario Clear Coat -L2K 769 K01 A2- |
Two-Part HS Optimum Plus Clear Coat -LZK 769 K07 A5- |
Two-Part HS Brilliant Plus Clear Coat -LZK 769 K05 A5- |
Two-Part HS Performance Clear Coat -LZK 769 K06 A5- |
Two-Part HS Mixed Paint/Top Coat -L2K 074/073...- |
Two-Part HS Hardener, Long -LHA 009 047 A3- |
Two-Part HS Hardener, Extra Long -LHA 009 048 A3- |
Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052
A3- |
Two-Part VHS Hardener, Extra Long -LHA 009 053 A2- |
For hardener, refer to the technical application
instructions here
→ Chapter „Hardener“. |
Two-Part Thinner -LVE 009 001 A5- |
Two-Part Thinner, Long -LVM 009 300 A2- |
Two-Part Thinner, Special -LVM 009 200 A2-/-LVM 009 200 A5- |
Clear Coat Additive -LVM 007 000 A2- |
Gloss Level Adjustment/Matting and Application Instructions |
Note
Refer to "Gloss Level Adjustment" (5.75) and "Repair Paint
Systems For Matte Painted Vehicles" (5.76). |
Note
The addition of Elastic Additive -ALZ 011 001- is omitted. |
Stir or shake the Matting Component -LVM 769 810 A2- in the
can well. |
With the two-part HS clear coat and two-part HS top coat,
mix the Matting Component -LVM 769 810 A2- according to
specification and infuse with hardener and thinner just before
processing. The processing of the ready-to spray mixture should
immediately follow. If the mixture remains in the mixing- or
spray gun receptacle for a longer period of time (15 minutes),
it should be stirred again before continuing to use
(separation). |
Adding the matting compound can influence the covering
capacity. |
It is absolutely necessary to test the respective mixture on
sheet metal to achieve the appropriate gloss level for the
vehicle. Gloss level measurements (60° angle) at adjacent parts
can also be helpful. |
A touch-up/repair of the matted clear coat within the
surface (for example, side part or clever repair) is not
possible. |
Dust inclusions cannot be polish out, so therefore ensure
that absolute cleanliness is maintained during the entire
painting process. |
Apart from color-dependent differences, the actual gloss
level is influenced by different factors. In the following
comparison, various additional parameters and their effect on
the gloss levels are represented. |
|
|
|
Higher Gloss Level |
Lower Gloss Level |
shorter hardener |
longer hardener |
shorter thinner |
longer thinner |
higher processing
viscosity |
lower processing viscosity |
higher dry layer
thickness |
lower dry layer thickness |
shorter ventilation time |
longer ventilation time |
forced drying |
Air drying |
Influencing Factors on the Gloss Level: |
Using different hardeners, thinners, application types,
drying conditions and layer thicknesses lead to different gloss
levels (up to 20%). |
|
|
|
Final drying time with forced drying is a minimum of 15 to
20 minutes |
|
|
|
Forced drying at +60 and 65 °C (140° and 149 °F) object
temperature for 45 minutes |
|
|
|
Personal Protective Equipment: |
Note the safety data sheets |
Wear the personal protective equipment during application |
|
|
|
Flashpoint: |
above +23 °C (73.4 °F) |
VOC value: 2004/42/IIB(e)(840)600 |
The EU limit for this product
(product category IIB.e) in ready-to-use form is a maximum of 840 g/L
volatile organic compounds. The VOC-value of this product in
ready-to-use form is a maximum of 600 g/L. |
The guaranteed shelf life of 48 months from date of
manufacture. Use no later than the date indicated on the label
and store in original container at +20 °C (68 °F). |
|
|
|
Definition:
Matting Component -ALN 775 106-
Edition 04/2013
Product Description
...
Definition:
Structuring Component, Fine -ALN 775 108-
Edition 04/2013
Product Description
...
Other materials:
Introduction
This chapter contains information on the following subjects:
→ Warning and indicator lamps
→ Engine oil specification
→ Checking the engine oil level and refilling engine oil
→ Engine oil consumption
→ Changing engine oil
Additional information and w ...
Vibration, Causes for Vibration
There are many causes for vibration. Vibration can also be
caused by tire wear, among other things. Tire wear caused by
driving does not always develop evenly over the entire tread.
Due to this, a slight imbalance develops which disturbs the
smoothness o ...
Evacuating and Charging Valve with Schrader Valve
Special tools and workshop equipment
required
Torque Wrench 1783 - 2-10Nm -VAG1783- with Torque Wrench
1783 - 1/4" Drive Ratchet -VAS6234-
WARNING
There is a dan ...
© 2016-2024 Copyright www.vwpolo.net