Volkswagen Polo Service & Repair Manual: Two-Part Fine Filling Paste

Definition:
Two-Part Fine Filling Paste -LSP 784 002 A2-
Edition 06/2011
Product Description
The two-part fine filling paste is a very fine thixotropic polyester filling paste.
This filling paste is suitable for small repairs.
Application Instructions
Properties
Fine and non-porous
Removes easily
Sands easily
High elasticity for touching up synthetic surfaces
Base Surface
Suitable base surfaces:
Steel
Aluminum
Glass fiber reinforced plastics
Old paint and factory paint
Hardened two-part filler/two-part primers
Plastic parts glaze-primed with Two-Part Plastic Adhesive Filler -LKF 696 009 A2-/-LKF 696 040 A2- or Adhesion Promoter -ALO 822 000 10-
Primed surfaces with two-part polyester filling paste.
  Caution
This filling paste may not be applied to PVB (acid-hardening) adhesive primers or one-part primers (for example, synthetic resin).
Application on thermoplastic or elastic coatings is also not possible. In these cases, only apply filler paste to bare steel.
   
Pre-treatment of base surfaces:
–  Remove any grease and sand the surface.
–  Bare metallic base surfaces are to be insulated with Two-Part Wash Primer -LHV 043 000 A2- and then filled with Two-Part HS Performance Filler. Sand the filler after drying.
–  With UP-GF underbodies, clean components of any residual agents and sand the surface.
 

Two-Part Fine Filling Paste

–  Use a suitable cleaning agent before reworking to ensure a clean and residue-free surface.
 

Two-Part Fine Filling Paste

Processing
Application type:
–  Apply filling paste.
 

Two-Part Fine Filling Paste

Mixture ratio:
–  Add 2 to 3 % by weight Two-Part Hardener -LVM 018 000 A1/A2- or, especially when dealing with high temperatures, Two-Part Hardener, Long -LVM 018 100 A2-.
  Note
Avoid using excessive hardener paste, to prevent it from bleeding through, especially on daylight colors and light metallic colors.
Curing Time:
–  At +20 °C (68 °F) room temperature for about three to five minutes.
Reaction Temperature:
–  Minimum +5 °C (41 °F)
 

Two-Part Fine Filling Paste

Drying
Air Drying:
–  At +20 °C (68 °F) room temperature for about 20 to 30 minutes.
 

Two-Part Fine Filling Paste

Infrared drying:
Short-wave heaters for three minutes (at 50 % power)
Medium-wave heaters for five minutes.
 

Two-Part Fine Filling Paste

Sanding compatibility
In connection with the aforementioned drying time:
–  Dry-sand the pre-sanding with P180-240 grit sandpaper
–  Dry-sand the final sanding with P240-320 grit sandpaper
 

Two-Part Fine Filling Paste

–  While wet, sand the pre-sanding with P240-320 sandpaper
–  While wet, sand the final sanding with P600-800 sandpaper
  Note
When wet-sanding, make sure to wipe and dry off the surface.
Temperature resistance up to +80 °C (176 °F).
 

Two-Part Fine Filling Paste

Reworking
Recommended structure:
One-Part Wash Primer -LVM 044 007 A2-/-LVM 044 171 A2-
Two-Part Wash Primer -LHV 043 000 A2- and Two-Part HS Vario Filler
Two-Part Plastic Adhesive Filler -LKF 696 009 A2-/-LKF 696 040 A2-
Unelasticized Adhesion Promoter -ALO 822 000 10- and Two-Part HS Filler (for plastic parts)
–  Then paint over with the top coat.
 

Two-Part Fine Filling Paste

Personal Protective Equipment:
Note the safety data sheets
Wear the personal protective equipment during application
Characteristics
 

Two-Part Fine Filling Paste

Delivery Viscosity pasty
Flashpoint: Filling paste over 23 °C (73.4 °F)
VOC value: 2004/42/IIB(b)(250)170 The EU limit for this product (product category IIB.b) in ready-to-use form is a maximum of 250 g/L volatile organic compounds. The VOC-value of this product in ready-to-use form is a maximum of 170 g/L.
 
Storage
The guaranteed shelf life is 12 months from the production date. Use no later than the date indicated on the label and store in original container at +20 °C (68 °F).
   
Storage Conditions
–  Storage Temperature +20 °C (68 °F) (temperature should not exceed +30 °C (86 °F)).
 

Two-Part Fine Filling Paste

Two-Part Steel Filling Paste Set
Definition: Two-Part Steel Filling Paste Set -DA 787 300 A2- Edition 09/2012 Product Description ...

Two-Part Fine Filling Paste, Flexible
Definition: Two-Part Fine Filling Paste, Flexible -LSP 787 100 A1- Edition 07/2010 Product Description The T ...

Other materials:

Tires, Reinforced, Extra Load
Some time ago, the designation “Reinforced” was replaced with the designation “Extra Load” by some tire manufacturers. In countries outside Europe, this designation has been conventional for some time. There are no technical differences. ...

Waxing and polishing the vehicle
First read and observe the introductory information and safety warningsWaxing Waxing protects the paintwork. You will need to re-wax the vehicle with a good hard wax if water no longer clearly forms small drops and runs off the paintwork when it is clean. Even if a wax solution is used regul ...

Refrigerant Circuit, Converting R12 to R134a and Servicing
  Note The laws and regulations listed below are applicable in Germany. Different or additional laws and regulations may apply in other countries. Addresses in other countries can be obtained from the relevant au ...

© 2016-2019 Copyright www.vwpolo.net