Volkswagen Polo Service & Repair Manual: Two-Part MS Matte Clear Coat
| Two-Part MS Matt Clear Coat -L2K 769 020 A2- |
| Two-part MS matt clear coat is a clear coat from the
two-part acrylic system. |
| Can be cured with HS and VHS products |
| Gloss grade adjustments with two-part HS clear coats are
possible. |
| Ideally suited for painting plastic |
 Note
| The use of Two-Part MS Matt Clear Coat -L2K 769 020 A2-
should be limited to small surfaces (passenger vehicle
attachments). |
| Suitable preliminary coatings: |
|
|
|
| Two-Part HS Hardener -LHA 009 041 A3- |
| Two-Part HS Hardener, Long -LHA 009 047 A3- |
| Two-Part HS Hardener, Extra Long -LHA 009 048 A3- |
|
|
|
| Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5- |
| Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052
A3- |
| Two-Part VHS Hardener, Extra Long -LHA 009 053 A2- |
Note
| Using varying HS/VHS hardeners and thinners results in
different gloss grades. |
|
|
|
| The clear coat should be carefully agitated before removing
the material. |
| Two-Part Thinner -LVE 009 001 A5- |
| Two-Part Thinner, Long -LVM 009 300 A2- |
| Two-Part Thinner, Special -LVM 009 200 A2-/-LVM 009 200 A5- |
|
|
|
| Processing time/pot life: |
| – |
Ready to spray in 4 hours at +20 °C (68 °F). |
|
|
|
| – |
Processing viscosity at +20 °C (68 °F) material temperature
is the mixing viscosity for “Compliant” and “HVLP”. |
| Processing viscosity 4 mm gravity feed spraygun “Compliant”
and “HVLP”: |
| DIN 4 mm: 14 to 16 seconds |
| ISO 4 mm: 28 to 33 seconds. |
|
|
|
| Add 25 % HS hardener (3:1) and 30 % VHS hardener (5:1) at
+20 °C (68 °F) material temperature |
| – |
Use a measuring stick to mix when pouring in the thinner. |
|
|
|
| – |
Set spray nozzle (see manufacturer's information):
“Compliant” and “HVLP” to 1.3 to 1.4 mm. |
| – |
Set spray pressure (see manufacturer's information):
“Compliant” to 2.0 to 2.5 bar. |
| – |
Set atomizing pressure (see manufacturer's information):
“HVLP” 0.7 bar. |
|
|
|
| – |
Apply one complete preliminary spray application, allow to
ventilate for 15 to 20 minutes and then finish painting. |
| – |
The prescribed layer thickness is 50 to 60 µm. |
Note
| Using varying application types results in different gloss
grades. |
|
|
|
| Air dry at +20 °C (68 °F) room temperature: |
| Dust dry after 2 to 2.5 hours |
| Ready for assembly after 5 to 6 hours |
|
|
|
| Final drying time with forced drying is a minimum of 15 to
20 minutes |
|
|
|
| Forced dry at +60 °C (68 °F) object temperature for 40 to 45
minutes |
|
|
|
| Personal Protective Equipment: |
| Note the safety data sheets |
| Wear the personal protective equipment during application |
|
|
|
| Flashpoint: |
above +23 °C (68 °F) |
| VOC value: 2004/42/IIB(e)(840)580 |
The EU limit for this product
(product category IIB.b) in ready-to-use form is a maximum of 840 g/L
volatile organic compounds. The VOC value of this product in
ready-to-use form is a maximum of 580 g/L. |
| The guaranteed shelf life of Two-Part MS Matt Clear Coat
-L2K 769 020 A2- is 24 months from date of manufacture. Use no
later than the date indicated on the label and store in original
container at +20 °C (68 °F). |
|
|
|
Definition:
Two-Part HS Clear Coat -L2K 769 500 A5-
Edition 10/2012
Product Description
...
Definition:
Two-Part HS Vario Clear Coat -L2K 769 K01 A5-
Edition 06/2013
Product Description
...
Other materials:
Parking Aid Sensor, Painting
The following parameters must be met when painting to avoid
malfunctions in the parking aid sensor (parking aid system):
New Part, Painting
Maximum coat thickness 125 µm; the coat thickness must
always be measured ...
Coolant specification
First read and observe the introductory information
and safety warningsThe cooling system is filled at the factory with a mixture
of specially prepared water and at least 40% coolant additive G 13
(TL-VW 774 J). The coolant additive is dyed purple. This mixture of water and coolant
additive ...
Tires, Reinforced, Extra Load
Some time ago, the designation “Reinforced” was replaced
with the designation “Extra Load” by some tire manufacturers. In
countries outside Europe, this designation has been conventional
for some time. There are no technical differences.
...
© 2016-2024 Copyright www.vwpolo.net
Two-Part HS Clear Coat
Two-Part HS Vario Clear Coat