Volkswagen Polo Service & Repair Manual: Two-Part Diamond Aluminum Filling Paste
| Two-Part Diamond Aluminum Filling Paste, Powder -DA 004 200
A2- |
| Two-Part Diamond Aluminum Filling Paste, Hardener -DA 004
201 A1- |
| Two-Part Diamond Aluminum Filling Paste, Hardener -DA 004
211 A1- |
| This filling paste is a polyester filling paste suitable for
all types of applications and especially for use in repairing
aluminum panels. |
| It is designed for use in automobile repairs. |
| This filling paste is pliable and sandable while maintaining
a high degree of firmness and temperature stability, which makes
it especially suitable to be painted over. |
 Note
| The Hardener -DA 004 211 A1- must be used at temperatures
over 30 (86 °F) and / or with a relative humidity over 80 %. |
|
|
|
| Pre-treatment of base surfaces: |
|
|
|
| – |
Carefully remove any grease and sand the base surface. The
base surfaces must be prepared using the
→ Chapter „Pneumatic Brush Grinder Set -VAS6446-“.
This means down to the bare metal with P40 grit sandpaper. If
necessary, clean the dirty surface once again and then remove
any cleaning residue again using the brush grinder. |
|
|
|
| – |
Both components are mixed in a ratio of 1 part by volume of
hardener liquid and 2.5-3 parts by volume of powder or 10 grams
of hardener liquid to 25 grams of powder to create a product
that can be spread. |
Note
| Avoid using too much hardener liquid, since this can
negatively affect the final strength and adhesion of the filling
paste. |
| – |
Pot life at +20 (68 °F) room temperature for approximately
four to six minutes |
|
|
|
| – |
Dry for approximately ten minutes. |
| – |
Cure using the short-wave IR heater. |
| Pre-hardening: 10 minutes at 50 °C (122 °F) |
| Hardening 1st step: 10 minutes at 75 °C (167 °F) |
| Hardening 2nd step: 10 minutes at 85 °C (185 °F) |
|
|
|
| – |
Use the body plane to remove any visible excess material
before the thermal final curing process. Then use P80 grit dry
sandpaper to sand the contours. |
Note
| Use only in well ventilated spaces. |
| The wearing of protective gloves and dust masks is
recommended. |
| The use of a grinding dust extractor is recommended. |
|
|
|
| Delivery Viscosity |
Powder + Hardener Liquid |
| Flashpoint: |
Hardener 33 °C (91.4 °F) |
| Powder is not applicable |
| The guaranteed shelf life is 12 months from the production
date. Use no later than the date indicated on the label and
store in original container at +20 °C (68 °F). |
|
|
|
| – |
Store in a cool and dry place. |
| – |
Storage temperature +20 °C (68 °F). |
|
|
|
Part names:
Two-Part IR Premium Filling Paste -LSP 787 220 A1-
Two-Part IR Premium Filling Paste -LSP 787 220 A2-
...
One-Part Anti-Corrosion Wash Primer
Definition:
One-Part Anti-Corrosion Wash Primer -ALN 002 003 10-
...
Other materials:
Infrared Dryer -VAS6876
Definition:
Infrared Dryer -VAS6876-
Product Description:
The infrared dryer is used to dry paste, filler, base paint,
top coats and clear coats on vertical and horizontal surfaces.
...
Introduction
This chapter contains information on the following subjects:
→ Preparing for a journey and driving safely
→ Driving abroad
→ Driving through water on roads
Depending on where the vehicle is used, it could be a good idea to have an engine
and transmission guard insta ...
Changing bulbs in the front headlights (halogen H7)
Fig. 180 Rear view of the
right-hand H7 front headlight: dipped beam ①, turn signal ②, and main beam and
side light ③
First read and observe the introductory
information and safety warnings
The actions should only be carried out in the speci ...
© 2016-2024 Copyright www.vwpolo.net
Two-Part IR Premium Filling Paste
Primer Metal